fig6
Figure 6. (A) Activation of different slip systems in differently oriented (α2+γ) lamellar structures relative to the load axis (on the left) and Schmid factor variation of different slip systems in α2/γ lamellar structures as they deviate from the load axis within an angle range of 0°-90° (on the right). (Reproduced from Ref.[68][68]); (B) XRD profiles of differently oriented PST-TiAl alloys deformed at room temperature. (Reproduced from Ref.[14][14]). XRD: X-ray diffraction.