From: Effect of elemental segregation and minor phase on mechanical properties of as-cast super-thick steels studied using in-situ synchrotron X-ray and neutron diffraction

$Effect of elemental segregation and minor phase on mechanical properties of as-cast super-thick steels studied using <i>in-situ</i> synchrotron X-ray and neutron diffraction$

Figure 6. In-situ neutron diffraction measurements of the Q370 sample during tensile testing: (A) Neutron diffraction patterns in the loading direction, clearly showing the (200) peak of retained austenite in the thicker specimen. (B) Evolution of the (200) reflection from retained austenite under various applied stresses.