From:  Hot isostatic pressing induced precipitation strengthening at room and high temperature of Ni-Fe-Cr-Al-V high-entropy alloy manufactured by laser powder bed fusion
Hot isostatic pressing induced precipitation strengthening at room and high temperature of <InlineParagraph>Ni-Fe-Cr-Al-V</InlineParagraph> high-entropy alloy manufactured by laser powder bed fusion

Figure 14. Misorientation between dislocation substructures in LPBF-processed HEA: BF image of dislocation substructures and SAED patterns in [011] zone axes corresponding to areas I and II, respectively.

Microstructures
ISSN 2770-2995 (Online)
Navigation
Follow Us
Navigation

Committee on Publication Ethics

https://publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/

Committee on Publication Ethics

https://publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/
partners@oaepublish.com Company Contact Us
Discover Content
Follow OAE
Twitter
Facebook
LinkedIn
YouTube
BiLiBiLi
WeChat
© 2016-2024 OAE Publishing Inc., except certain content provided by third parties