From: The effect of chromium content on the corrosion behavior of ultrafine-grained Cr_xMnFeCoNi high-entropy alloys in sulfuric acid solution

The effect of chromium content on the corrosion behavior of ultrafine-grained Cr<i><sub>x</sub></i>MnFeCoNi high-entropy alloys in sulfuric acid solution

Figure 6. Surface morphology (A₁-D₁, A₂-D₂) and AFM height images (A₃-D₃) of the Cr_xMnFeCoNi (x = 0, 0.6, 1, and 1.5) HEAs after polarization tests in a 0.5 M H₂SO₄ solution at room temperature.

Microstructures

ISSN 2770-2995 (Online)

[email protected]

Navigation

Sitemap

Navigation

Sitemap

Committee on Publication Ethics

https://members.publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/

Committee on Publication Ethics

https://members.publicationethics.org/members/microstructures

Portico

All published articles are preserved here permanently:

https://www.portico.org/publishers/oae/

Discover Content

Strategic Collaborators

Follow OAE

Privacy Cookies Terms of Service